Stainless Steel, Steel Coil, Steel Coil 430 manufacturer / supplier in China, offering Stainless Steel Coil 430 From Hannstar Industry, Nickel Strip & Foil /Nickel Colil for Battery Industry, Hot Dipped Galvanized Steel Pipe and so on.

Gold Member Since 2015
Audited Supplier

Stainless Steel Coil 430 From Hannstar Industry

Get Latest Price
Min. Order / Reference FOB Price
20 Tons US $1,100-2,000/ Ton
Port: Qingdao, China
Production Capacity: 10000 Metric Ton/Metric Tons Per Month
Payment Terms: L/C, T/T, Western Union
Type: Stainless Steel Sheets
Standard: ASTM, AISI, GB, JIS, DIN, EN
Grade: 400 Series
Certification: ISO
Shape: Flat
Technique: Cold Rolled

You Might Also Like

Loading...

Basic Info

Model NO.: stainless steel
Surface Treatment: Polished
Thickness: 0.3-6mm
Trademark: Hannstar Industry
Transport Package: Seaworthy Package for Export
Specification: Width: 1000-2000mm
Origin: China

Product Description

STAINLESS STEEL COIL 430
Technical: Hot rolled
Surace:No.1/1U
Thickness:3.0-12.0   Width:1000/1219/1500mm
Min qty:10mt

Technical:cold rolled 
Surface:2B
Thickness:0.08-1.2mm  width:4.5-630mm
Thickness:0.3-3.0mm   width<1500mm
Min qty:5mt


Chemical Composition
TYPECSiMnPSNiCr
4300.1201.001.000.0400.0300.7516.00~18.00


Product Details

TYPE 430 STAINLESS STEEL 
Type 430  are low carbon ferritic stainless steels which, in mildly corrosive environments or atmospheric exposures, have corrosion resistance approaching that of some nickel stainless steels. These alloys are oxidation resistant at elevated temperatures. Types 430 and 434 are ductile, do not work harden readily, and can be formed using a variety of roll forming or mild stretch bending operations as well as the more common drawing and bending processes.

Machining
Types 430  should be machined at speeds about 60% of those used for a similar operation on reference type B1112. Your Allegheny Ludlum representative will furnish information on free-machining modifications of these alloys.

Welding 
Allegheny Types 430  can be welded by all commercial processes normally used to weld stainless steels. For best results the stainless steel parts to bejoined must be completely free of grease, oil or other surface contamination. Satisfactory joints can be made with austenitic weld deposits of base metal. If the welded structure is to be subjected to thermal cycling, filler wire of the base metal composition should be used to avoid differences in thermal expansion which can cause bucking.
Welding these alloys will cause a decrease in ductility of the weld and heat affected zones due to the formation of martensite during cooling. The weld heat affected zone will also suffer a marked loss of corrosion resistance in some environments, Both ductility and corrosion resistance can be restored by annealing.
Both welding and subsequent annealing will form a scale or heat tint of these alloys. These discolorations must be completely removed to realize maximum corrosion resistance.

APPLICATIONS
These alloys are used in a variety of interior and exterior trim applications where corrosion resistance is more important than high strength. Typical applications are sinks and sink rims, appliance trim and counter tops.
For supplementary information on product forms, applications, conditions, sizes, finishes, coatings and pattern finishes see the Allegheny Ludlum Stainless Steel Brochure Series SS91.98. Information on specifications is contained in pamphlet SS90.

Send your message to this supplier

*From:
*To:
avatar Mr. Aaron Zhang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

People who viewed this also viewed